Superior Electrochemical Properties of Nanofibers Composed of Hollow CoFe2 O4 Nanospheres Covered with Onion-Like Graphitic Carbon.

Nanofibers composed of hollow CoFe2 O4 nanospheres covered with onion-like carbon are prepared by applying nanoscale Kirkendall diffusion to the electrospinning process. Amorphous carbon nanofibers embedded with CoFe2 @onion-like carbon nanospheres are prepared by reduction of the electrospun nanofibers. Oxidation of the CoFe2 -C nanofibers at 300 °C under a normal atmosphere produces porous nanofibers composed of hollow CoFe2 O4 nanospheres covered with onion-like carbon. CoFe2 nanocrystals are transformed into the hollow CoFe2 O4 nanospheres during oxidation through a well-known nanoscale Kirkendall diffusion process. The discharge capacities of the carbon-free CoFe2 O4 nanofibers composed of hollow nanospheres and the nanofibers composed of hollow CoFe2 O4 nanospheres covered with onion-like carbon are 340 and 930 mA h g(-1) , respectively, for the 1000th cycle at a current density of 1 A g(-1) . The nanofibers composed of hollow CoFe2 O4 nanospheres covered with onion-like carbon exhibit an excellent rate performance even in the absence of conductive materials.