The Role of CHPD and AIMI processing on enhancing J C and transverse connectivity of in-situ MgB2 strand.

Research into in-situ MgB2 strand has been focused on improvements in J C through reduction of porosity. Both of cold-high-pressure-densification (CHPD) and advanced-internal-magnesium-infiltration (AIMI) techniques can effectively remove the voids in in-situ MgB2 strands. This study shows the nature of the reduced porosity for in-situ MgB2 strands lies on increases in transverse grain connectivity as well as longitudinal connectivity. The CHPD method bi-axially applying 1.0 GPa and 1.5 GPa yielded 4.2 K J CM∥s of 9.6 × 104 A/cm2 and 8.5 × 104 A/cm2 at 5 T, respectively, with compared with 6.0 × 104 A/cm2 for typical powder-in-tube (PIT) in-situ strand. Moreover, AIMI-processed monofilamentary MgB2 strand obtained even higher J Cs and transverse grain connectivity than the CHPD strands.