Study on triphase of polymorphs TiO2 (anatase/rutile/brookite) for boosting photocatalytic activity of metformin degradation.

The elution of pharmaceutical products such as metformin at higher concentrations than the safe level in aquatic systems is a serious threat to human health and the ecosystem. Photocatalytic technology using TiO2 semiconductors potentially fixes this problem. This study aims to synthesize triphasic anatase-rutile-brookite TiO2 using ultrasound assisted sol-gel technique in the presence of acid and its application to photodegradation of metformin under UV light irradiation. Based on X-ray diffraction analysis, a TiO2 sample consisted of anatase (76%), rutile (7%), and brookite (17%) polymorph (A76R7B17) that was fully crystallized. Scanning electron microscopy (EM)-energy dispersive X-ray spectra results showed agglomerated triphasic A76R7B17 with irregular spherical clusters. Transmission EM results revealed that the crystal size of A76R7B17 was 4-14 nm. The Brunauer-Emmett-Teller analysis showed the sample's specific surface area of 149 m2 g-1. The degradation test of metformin demonstrated that the A76R7B17 exhibited a 75.4% degradation efficiency after 120 min under UV light irradiation, significantly higher than using biphasic and single-phase TiO2 photocatalysts. This difference could be attributed to the heterojunction effect of triphasic materials that effectively reduced electron-hole recombination rate as well as the combination of effective electron transfer from conduction band of brookite and anatase and the utilization of wider range of UV-visible light using rutile.